| EPOXIES |
Data Sheets |
(ASTM Test Method) |
|
(D-1084) |
|
(D-1002) |
(D-1876) |
(D-256) |
|
|
One Minute®
Epoxy Gel |
|
• Thixotropic, high strength epoxy adhesive
• Fast fixturing |
Amber |
70,000 |
0:45 |
3/4 - 1 |
1/2-3/4 |
-40-200 |
1,600 |
2-3 |
4.5 |
1 |
| 5 Minute®
Epoxy |
Technical Data Sheet |
•
Rapid curing
• General purpose
• Clear rigid bond or coating in minutes
•
Bonds metals, fabrics, ceramics, wood, concrete |
Light Amber |
10,000 |
3-6 |
10-15 |
3/4 - 1 |
-40-200 |
1,900 |
2-3 |
5.5 |
1 |
| 5 Minute®
Epoxy FR |
|
•
Flame retardant
• Rapid curing
• Clear, rigid bond in minutes |
Gray |
115,000 |
3-5 |
10-15 |
2-3 |
-40-200 |
2,800 |
2-3 |
5.5 |
1 |
| 5 Minute®
Epoxy Gel |
Technical Data Sheet |
•
Non-migrating creamy gel
• Fast curing
• Fills gaps
• Bonds metals and rigid
substrates |
Amber |
150,000 |
4-7 |
10-15 |
3/4 - 1 |
-40-200 |
2,500 |
2-3 |
6.5 |
1 |
10 Minute®
Epoxy
Black and Clear |
Technical Data Sheet |
• Flexible
• High peel strength
• Ideal for
aluminum, steel, brass, galvanized steel, plastics, epoxy and FRP composites |
Black |
90,000 |
10 |
20 |
1 1/2 |
-67-200 |
2,400 |
20-25 |
10 |
5 |
| Clear |
80,000 |
10 |
20 |
1 1/2 |
-67-200 |
2,400 |
20-25 |
10.0 |
5 |
| 2 Ton® Epoxy |
Technical Data Sheet |
•
Adhesive/potting compound
• High Strength
• Non-shrinking
• High clarity,
good impact strength, & water resistance
• Weather & solvent
resistant
• Wide temperature range |
Clear |
8,000 |
8-12 |
30-35 |
2 |
-40-200 |
2,250 |
2-3 |
6.5 |
1 |
| Epoxy Plus™ 25 |
Technical Data Sheet |
•
Rubber toughened, non-corrosive structural adhesive
• Bonds metals, ceramics
composites,
& many thermoset plastics
• 25 minute working time |
Gray |
70,000 |
25 |
210 |
24 |
-40-200 |
2,750 |
20-25 |
10.0 |
20 |
| HP 250 |
Technical Data Sheet |
• High Performance structural adhesive
for assembly applications
• High shear
strength & impact toughness
• High chemical, fatigue and stress
resistance
• Bonds dissimilar substrates |
Straw |
105,000 |
65 |
5 |
24 |
-67-250 |
3,200 |
35-40 |
12.0 |
25 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|