EPOXY ADHESIVES/ HUNTSMAN
| Product designation |
Data Sheets |
Selected
specifications |
Mixed
Viscosity |
Work Life |
Curing Class |
Typ Service Temp. |
Lap Shear
Strength |
T-Peel |
Characteristics |
| Conditions |
|
RT |
RT |
|
AI/AI |
|
| Unit |
|
(min) |
(min) |
(ºC) |
(ºC) |
(psi) |
(pli) |
| EPOXY ADHESIVES - Araldite |
| Araldite® 204 |
Technical Data Sheet |
ABR2-0048 |
3 500 000 |
- |
120 or 150
or 170 |
90 |
1 740/1 450 |
- |
1-part foaming adhesive,
fills
voids
(for core splicing),
extrudable paste |
| Araldite®/Epibond®
420 A/B |
Technical Data Sheet |
ASNA 4125,
lss B/BMS 5-107 |
35 000-45 000
(semi-paste) |
60-70 |
RT |
82 |
3 500-5 100/580 |
22 |
Very high shear & peel
strengths, bonds most metals, wood, rubber, composites, plastics |
| Araldite® 2011 A/B |
Technical Data Sheet |
ABR2-1079;
DAN 1284-01 |
45 000
(non-sag paste) |
120 |
RT |
60 |
3 625/1 160 |
28 (roller) |
Long open time,
high shear/peel
strength,
dynamic load bearing,
electrically insulating, pumpable |
| Araldite® 2013 A/B |
Technical Data Sheet |
ABP 5-1158, iss 2 |
Thixotropic Paste |
65 |
RT |
60 |
3 000/700¹ |
23(roller) |
Metallic appearance,gap-filling
to 5mm good chemical & weather resistance,
bonds to metal, ceramic,
rubber & plastic |
| Araldite® 2014 A/B |
Technical Data Sheet |
ABP2-3094;
ABR2-0714 |
90 000 |
40 |
RT |
120 |
2 400/2 400 |
17 (roller) |
High temperature,
chemical &
water resistant,
gap-filling, bonds to wide
variety of substrates |
| Araldite® 2015 A/B |
Technical Data Sheet |
ABR2-1081 |
Thixotropic
(non-sag paste) |
35 |
RT |
80 |
3 500/1 050¹ |
25(roller) |
Toughened, non-sag, gap-filling
to 10mm, high shear & peel strength |
| Araldite® AV 4415/HV 4416; XD 4510/XD 4511 |
|
KIWA potable water;
FPI
Europe |
Non-flow paste |
90 |
40-150 |
180 |
2 500/2 500 |
9-34 (roller) |
V high temperature &
good
chemical resistance, gap-filling, bonds to wide range of substrates |
|
|
|
|
|
|
|
|
|
|
| Product
designation |
Data Sheet |
Selected
specifications |
Mixed Viscosity |
Work Life |
Curing Class |
Typ Service
Temp. |
Lap Shear Strength |
T-Peel |
Characteristics |
| Conditions |
|
RT |
RT |
|
|
AI/AI |
|
| Unit |
|
(min) |
(min) |
(ºC) |
(ºC) |
(psi) |
(pli) |
| EPOXY ADHESIVES - Epibond |
| Epibond® 104 A/9831 |
|
AS 2149009-R;
BS
201-AA |
Paste |
3-4 |
RT |
93 |
2 000-2 800/600-1
000² |
- |
Quick-set to long
work life with
3 hardeners (by increasing gel time), non-flow paste,
gap-filling |
| Epibond® 104 A/946 |
|
20 |
| Epibond® 104 A/104 B |
|
30-40 |
| Epibond® 156 A/B |
Technical Data Sheet |
Motorola 11-14235
ACL |
Soft paste |
20-50 |
RT |
121 |
2 000/1 950 |
- |
RT Cure, low shrinkage, good electrical insulator, good for smoothing, filling (e.g. laminates,
edges, radomes) |
| Epibond® 1210 A/B |
|
LAC 40-4093, CI B |
Semi-paste |
50-75 |
RT |
93 |
2 500/300 |
- |
Low outgassing
(spacecraft),
flexibility can be varied |
| Epibond® 1210 A/9861 |
|
LAC 30-4639-0200 |
Semi-paste |
35-60 |
RT |
149 |
2 800/2 500² |
- |
Low outgassing
(spacecraft),
good high temperature properties |
| Epibond® 1217 A/B |
|
HMS 16-1068 CI 8B |
Paste |
4-8 |
RT |
66 |
2 500/300 |
- |
Fast set, translucent, 1:1
mix ratio |
| Epibond® 1534 A/B |
|
BMS 5-126, Ty 2, Cl 1 |
2 000 |
120 |
RT |
82 |
3 000/575 |
- |
Long work life, low
viscosity,
high strength good fluid resistance |
| Epibond® 1539 A/B |
|
BMS 5-126, Ty 6, Cl 1 |
Paste |
120 |
RT |
82 |
2 500/800 |
- |
Bonds to plastic, metal,
fiberglass reinforced composite |
| Epibond® 1544 products |
|
BMS 5-126, Ty IV,
Cl 1 or 4,
Gr B |
Semi-paste |
10-20 |
RT |
93 |
2 600/600 |
- |
RT cure, early green
strength, gap filling, flame retardant |
| Epibond® 1546 A/B |
|
- |
Semi-paste |
5-7 |
RT |
60 |
3 000/- |
9(T); 18(roller) |
Very fast cure, good peel
strength,
1:1 mix ratio
(w/w or v/v cartridge dispensed) |
| Epibond® 1559 products |
|
Airbus SIL 53-035,
App4;
SS-8640 |
80 000 |
6 |
RT |
70 |
2 900/3 00¹ |
- |
Fast RT or low temp cure, flame retardant, 1:1 mix ratio |
| Epibond® 1565 A/B |
|
Boeing
D800-10411-1 PPD6-1 |
25 000
(non-sag paste) |
720 |
177 |
150-177 |
1000/- |
- |
Long work life, high
temperature
performance, thixotropic paste |
| Araldite® 1570 A/B |
|
AIMS 10-04-006 |
220 000 |
60 |
RT |
80 |
2 400/600 |
- |
Polyolefin bonding, flame
retardant (FAR 25.856) |
| Epibond® 1590 A/B |
|
AIMS 10-09-001 |
70 000 |
30 |
40-100 |
177 |
5 800/3 400³ |
24-33 (roller) |
Roughened, low sag, 177°C performance |
| Epibond® 1590-3mm A/B |
Technical Data Sheet |
AIMS 10-07-002 |
2 000 000 |
50 |
70 |
80 |
4 500/3 230 |
16.4 (roller)r) |
Gap-filling to 3mm, high
strength,
good environmental stability |
| Epibond® 1590 FST A/B |
|
DANs 1199-01 &
1187-01 |
120 000 |
60 |
RT |
120 |
3 200/1 600 |
22 (roller) |
Meets FAR 25.853 flame
resistance criteria including smoke density & heat release, good hot/wet
mechanical performance |
| Epocast® 1635 A/B |
|
BMS 5-28, Type 31
(QPL
pending) |
Semi-paste |
60 |
93 |
177 |
2 500-3 000⁴/ 2
500-3 000²,⁴ |
Dynamic fatigue resistance for miss-drilled hole filling, high temperature lap shear & compressive
strength |
| Epibond® 8543 C/B |
|
BMS 5-123, Ty 1, Cl3 |
Non-sag paste |
3 |
7-RT |
83 |
2 000/500 |
- |
Very fast set, 1:1 mix
ratio |
|
|
|
|
|
|
|
|
|
|
|