 RTV SILICONES   . . . GELS 2 PART ADDITION CURE. . .GELS 1 PART ADDITION CURE. . GELS 2 PART ADDITION CURE - CLEAR
ge silicones
 Silicone Gels

Our gels may preserve dielectric integrity and protection of delicate electronic circuit assemblies operating in harsh environments.
They can offer external shock and vibration protection/ dampening, mechanical cushioning, excellent moisture protection and low shrinkage, and they are self-healing
    <<BACK
<< BACK   2 Part Addition Cure1 Part Addition Cure
        UL94 V-1
RTV6186 RTV6196 TSE3070 TSE3051 TSE3051FR
Data Sheets Technical Data Sheet Technical Data Sheet Technical Data Sheet Technical Data Sheet Technical Data Sheet
Features High strength, fast heat curing, tough gel; Good tear resistance; Extended room temperature pot-life (8+ hours) can benefit use on non-automated production lines. Fast curing, low viscosity silicone gel; Requires the use of dispensing equipment. Low viscosity, high elongation gel. Fast heat curing, low viscosity potting gel. Flame retardant, fast heat curing, low viscosity potting gel. UL94 V-1 recognition at 3.0mm.
Mix Ratio
(base to curing agent by weight) 		1:1 1:1 1:1 1-component 1-component
Color
(Final Product)		 Translucent Translucent Translucent Translucent Translucent
Viscosity (cps) 750 750 800 700 700
Useful Temperature Range -50 to 205°C
(-58 to 400°F) 		-50 to 205°C
(-58 to 400°F) 		-50 to 205°C
(-58 to 400°F) 		-50 to 200°C
(-58 to 392°F) 		-50 to 200°C
(-58 to 392°F)
Specific Gravity 0.98 0.98 0.98 0.97 0.97
Refractive Index 1.406 1.406 1.404 1.404 1.404
Hardness, Penetration (mm) 6.0 6.0 – – –
Hardness, Penetration, ASTM D 1403 (mm) – – 65 85 85
Thermal Conductivity (W/mK) 0.19 0.19 0.17 0.17 0.17
Coefficient of Thermal Expansion (Linear CTE, cm/cm °C (in/in °F)) 27 x 10-5
(15.3 x 10-5) 		27 x 10-5
(15.3 x 10-5) 		– – –
Cubical Expansion (I/°C) – – 0.56 x 10-3 0.56 x 10-3 0.56 x 10-3
Dielectric Strength
(75 mils, kV/mm, V/mil)) 		20.5
(500) 		20.5
(500) 		18
(400) 		18
(400) 		18
(400)
Dielectric Constant
(1 kHz)		 2.8 2.8 2.7 2.8 2.8
Dissipation Factor
(1 kHZ)		 0.001 0.001 0.002 0.001 0.001
Volume Resistivity
(ohm-cm) 		1.0 x 1015 1.0 x 1015 1.0 x 1015 1.0 x 1015 1.0 x 1015
Processing Work (Pot) Life @ 23°C >8 hours 15 minutes 4 hours 2 weeks 2 weeks
Cure Time 25°C – < 2 hours < 24 hours – –
65°C 4 hours 1 hour 45 minutes – –
100°C 1 hour 10 minutes – 3 hours 3 hours
125°C – – – 2 hours 2 hours
150°C 15 minutes 5 minutes – 1 hour 1 hour
  • Note: Additional information may be available on the technical datasheet. This chart contains typical property values and actual values or results may vary.
    (1)
    Not intended for use with RTV6156 which was designed for low temperature performance. Changes to the mix ratios can either shorten or lengthen the pot life of the catalyzed mixture.