| HIGH PERFORMANCE |
| |
RTV142 |
RTV1673LV |
RTV6700++ |
RTF5308 |
RTV5810 Series++ |
RTV120 Series++ |
| Data Sheet |
Technical Data Sheet |
Technical Data Sheet |
Technical Data Sheet |
|
Technical Data Sheet |
|
| Features |
Low volatile, paste adhesive. |
Low volatile, paste adhesive.Non-corrosive to aluminum and steel. |
Paste adhesive. UL94 HB recognition. |
Fast curing, paste adhesive. Capable of being mechanically
foamed. |
Fast curing, paste adhesive designed to provide quick initial adhesion build. UL94 HB recognition. |
ste adhesive. UL94 HB recognition. MIL-A-46146B. |
Typical Applications
(include but not limited to) |
Electronic adhesive; Electronic gasketing;
Sealing and bonding. |
Gasketing; Under hood applications. |
May be suitable for applications in confined spaces; Applications requiring long work life for tooling of finished assemblies. |
Formed-in-place gaskets; Vertical and Horizontal applications; Hot/Cold thermal cycles; Expandable Silicone Foam per GM2224M2D2CF1, Type II. |
Assembly applications requiring high productivity; Sealed assemblies; May be suitable for applications in confined spaces. |
Sealing vertical joints; Electrical insulation of wires and terminals; Formed-in-place
gasketing. |
| Key Substrate Adhesion |
Primerless adhesion to many metals, plastics, masonry, wood, glass and ceramics. |
Primerless adhesion to many metals, plastics, masonry, wood, glass and
ceramics. Not recommended for use on polycarbonates and acrylics. |
Primerless adhesion to many metals, plastics, masonry, wood, glass and ceramics. Not recommended for use on polycarbonates and acrylics. |
Primerless adhesion to many metals, plastics, masonry, wood, glass and
ceramics. Not recommended for use on polycarbonates and acrylics. |
rimerless adhesion to many metals, plastics, masonry, wood, glass and ceramics. Not recommended for use on polycarbonates and acrylics. |
Primerless adhesion to many metals, plastics, masonry, wood, glass and ceramics. Not
recommended for use on polycarbonates and acrylics. |
| Cure Chemistry |
Alkoxy |
Modified Alkoxy. |
Modified Alkoxy |
Modified Alkoxy |
Modified Alkoxy |
Modified Alkoxy |
Color
(Final Product) |
White |
Black |
RTV6702: White
RTV6703: Black
RTV6708: Translucent |
Translucent |
RTV5812: White
RTV5813: Black
RTV5818: Translucent |
RTV122: White
RTV123: Black
RTV128: Translucent |
| Viscosity (cps)/ Application Rate (g/min) |
725 g/min |
750 seconds |
250 g/min |
290 g/min |
480 g/min |
600 g/min |
| Useful Temperature Range |
-60 to 205°C
(-75 to 400°F) |
-60 to 205°C
(-75 to 400°F) |
-60 to 205°C
(-75 to 400°F) |
60 to 205°C
(-75 to 400°F) |
-60 to 205°C
(-75 to 400°F) |
-60 to 205°C
(-75 to 400°F) |
| Specific Gravity |
1.09 |
1.06 |
1.04 |
1.04 |
1.04 |
1.04 |
| Hardness, Shore A Durometer |
34 |
28 |
18 |
22 |
21 |
30 |
| Tensile Strength (psi) |
550 |
360 |
225 |
305 |
275 |
250 |
| Elongation (%) |
400 |
560 |
450 |
485 |
500 |
350 |
Dielectric Strength
(75 mils, V/mil) |
500 |
500 |
409 |
– |
425 |
500 |
Dielectric Constant
(60 Hz) |
2.80 |
2.60 |
2.9 @ 100 Hz |
– |
2.8 @ 100 Hz |
2.80 |
| Volume Resistivity (ohm-cm) |
4.5 x 1015 |
2.0 x 1015 |
2.0 x 1015 |
– |
2.0 x 1015 |
4.0 x 1015 |
Processing:
Tack Free Time |
4 hours |
15 minutes |
25 minutes |
18 minutes |
15 minutes |
20 minutes |
| Cure Time@ 25°C (77°F)+ |
24 hours |
24 hours |
24 hours |
12 - 24 hours |
12 to 24 hours |
24 hours |